1. ZCCCT Original raw micro grain material, high hardness and
T.R.S.
a, Co: 10%,Wc:90%
b, TRS: >3600 N/mm2
c, HRA: 91.8-92.4, HRC:45/55/60/65
d, Grain size: 0.4-0.6μm
e, Helix angle: 30°-45 °
Diameter of cutting edge: 0.2-0.9mm; 1-20mm
Diameter of rods: 4-20mm Length: 50-100mm
Cutting Form: Square,Ball nose, Corner Radius, Taper Flute, etc.
Flutes No.: 1-6 .
2.Other products: drills,reamer, tool holders, ER collet, boring cutters, carbide
inserts, cutter heads,etc.
3.Application and usage
Suitable for Copper, Cast Iron, Carbon steel, Tool steel, Mould
steel, Die steel, Stainless steel, Plastic, Arcylic, etc.
4. Super coating:
TiSiN TiAlN AlTiN TiCN or Blue Nano Coating,
| Item | AlTiN | TiAiN | TiSiN | nAcO |
| Hardness(HV) | 3200 | 2800 | 3600 | 42(GPA) |
| Thickness(UM) | 2.5-3 | 2.5-3 | 3 | 3 |
| Oxidation Temp( ° ) | 900 | 800 | 1000 | 1200 |
| Friction | 0.3 | 0.3 | 0.45 | 0.4 |
| Color | Black | Violet | Copper | Blue |
improve tool life, reduce the coefficient of friction.
Our advantages:
1.Solid carbide lasting long life in hardened steels, Grain size
carbide, high toughness,high-wearing feature.
2.Non-standard can be customized according to customer's
requirements
3.We have produce ability to satisfy your orders,another
manufacturing bases will becompeleted in the near month
5.More than 20 years professional experience
Super raw material
| HRC45 | HRC55 | HRC60 | HRC65 |
| YG10X | YG10.2 &WF25(Taiwan) | K44 & K40 (German) | H10F (Sweden) |
Grain Size:0.7um
Co:10 %
Flexural strength: 3320N/mm2 | Grain Size:0.6um
Co:10 %
Flexural strength: 4000N/mm2 | Grain Size:0.5um
Co:12 %
Flexural strength: 4300N/mm2 | Grain Size:0.5um
Co:10 %
Flexural strength: 4300N/mm2 |
Super coating
| Item | AlTiN | TiAIN | TiSiN | nACo |
| Hardness(HV) | 3200 | 2800 | 3600 | 42(GPA) |
| Thickness(UM) | 2.5-3 | 2.5-3 | 3 | 3 |
| Oxidation Temp(°) | 900 | 800 | 1000 | 1200 |
| Friction Coeffient | 0.3 | 0.3 | 0.45 | 0.4 |
| Color | Black | Violet | Copper | Blue |